PE 100(N) Grade | Toosplast HDPE Polymer Compound

Description

PE100 (HM-CRP100N) is a natural pipe grade resin which is manufactured by suspension polymerization of ethylene monomer,  PE100 (HM-CRP100N) is a bi-modal high density polyethylene with 1-Butene as comonomer.

PE100 is the third generation of pipe grade PE.
It has an optimum balance of three key properties:

• Minimum Required Strength (MRS) – this provides long-term strength and creep resistance.
• Stress crack resistance (sometimes referred to as slow crack growth resistance).
• Rapid crack propagation resistance.

PE & HDPE PE100 Pipe Properties

• Minimum Required Strength (MRS): 10.0 MPa (1450 psi)
• Hydrostatic Design Basis (HDB) Pressure: 1600 psi (11 MPa)
• Allowable Compressive Strength: 7.93 MPa
• Tensile Strength at Yield: 23 MPa
• Elongation at Break: >600%
• Modulus of Elasticity (50 years): 200 MPa
• Flexural Modulus: 1000 MPa
• Poisson’s Ratio: 0.45
• Thermal Expansion Co-efficient: 1.3 x 10-4 °C-1

Friction Co-efficients:

• Colebrook-White: 0.00152mm
• Hazen-Williams: 150-155
• Manning: 0.009 (water); 0.010 (sewage)

Temperature Resistance of PE pipe

The properties of HDPE PE100 pipe are determined at standard temperatures of 20°C or 23°C. These properties can be significantly affected by temperature, so at higher temperature the properties, including MRS, decrease. At higher temperatures it may be necessary to apply reduction factors to MRS, and consequently MOP.

The Toos Plast PE100 granule is produced by best polymer raw materials and unique formulation. All Polymer compounds raw materials are made in Iran.

For more information please read the PE100 data sheet